Premium M Blade-6o Artificial Turf
90 oz, 1.75" Height, M Blade.
Premium M Blade-60 Artificial Turf acts like memory foam and provides exceptional softness and cushioning. Its strong blades are resilient and recover well. Turf temperature under the direct sun is lower than average. The material is resistant to wear and tear but did show signs of use.
See the results and test specifications below.
Meter showed 70 degrees of angle adjustment.
Softer than average.
The tennis ball jumped 15 inches. This grass provides double the cushion of office carpet.
Blades recovered 94%
The recorded temperature is 95 degrees. This is 15 degrees cooler than a 2 mm stainless steel plate under the same conditions.
Wear and Tear
Blades changed shape, recovered to 80%. Wear is visible. No structural damage to blades or backing is showing.
Every test we conduct is measured and compared to a test item for easier understanding.
- How do you measure turf softness?
We brush the turf 5 times with an angle measurement tool that is resistant to friction. The softer the turf, the less movement we will see on the ruler.
The fewer degrees on the ruler, the softer the turf.
- How do you measure cushion?
We drop a tennis ball #3 from 6 ft. above directly on the surface of the turf to measure the cushion. The less it bounces, the more cushion the artificial grass provides.
We compare results to the bounce carpet provides for clarity.
- How do you determine turf recovery?
We place a 30lb weight on the artificial grass material for 5 minutes, then wait 15 minutes at room temperature and measure blade length compared to the original.
- How do you measure temperature?
We measure the temperature under the direct sun after 30 minutes of exposure without wind.
As a data backup, we compare this to the temperature of a stainless steel plate under the same conditions.
- How do you assess wear and tear?
We apply an abrasive brush to the turf for a period of 30 seconds and observe the blade's structure afterward. We look for damage, twist, recovery, and blade structure deformation.